The Effect of Different Types of Aggregate and Additives on the Properties of Self-Compacting Lightweight Concrete
Main Article Content
Abstract
The major aim of this research is study the effect of the type of lightweight aggregate (Porcelinite and Thermostone), type and ratio of the pozzolanic material(SF and HRM) and the use of different ratios of w/cm ratio(0.32 and 0.35) on the properties of SCLWC in the fresh and hardened state. SF and HRM are used in three percentage 5%,10%, and 15% as a partial replacement by weight of
cement for all types of SCLWC. The requirements of self-compatibility for SCC are fulfilled by using the high performance superplasticizer (G51) at 1.2liter per 100 kg of cement. The values of air dry density and compressive strength at age of 28 days within the limits of structural lightweight concrete. The air dry density and compressive strength at age of 28 days for w/cm ratio(0.32) for SCLWC of Porcelinit aggregate are 1964 kg/m3 and 29.57 MPa, respectively. The corresponding values for the SCLWC of Thermostone aggregate are 1820 kg/m3 and 25.75 MPa, respectively. The results show that the HRM performance which is locally available is better
than SF in production of SCLWC.
Article Details
Section
How to Cite
References
Qusay, J.H " The effect of different types of aggregate and additives on the propertiesof Self-Compacting Lightweight Concrete" M.SC. Thesis, Baghdad University, February 2011.
• ACI Committee 213, "Gide for Structural Lightweight Aggregate Concrete", ACI 213R87, ACI Manual of concrete practice, Part 1, 1991, pp.213R-1-27.
• ACI Committee 211, "Standard Practice for Selecting Proportion for Structural Lightweight Concrete", ACI 211.2-98, ACI Manual of concrete Practice, Part1, 1998, pp.211.2-98
• ACI Committee 234, "Gide for the Use of Silica Fume in Concrete", ACI 234R-96, ACI Manual of concrete practice, Part 1, 1996, pp.234R-1-41.
• Advanced Cement Technology, LIC, "High Reactivity metakaolin engineered material admixture for use with Portland cement", 2002, pp.7, www.metakaolin.com, Email: sales@ metakaolin.com.
• ASTM C330-03," Standard Specification for Lightweight Aggregates for Structural Concrete", Annual Book of ASTM Standards,2003.
• ASTM C 494/C 494M – 05a, " Standard Specification for Chemical Admixtures for Concrete", Annual Book of ASTM Standards,2005.
• ASTM C 1240-03 " Standard Specification for Use of Silica Fume as a Mineral Admixture in Hydraulic-Cement Concrete, Mortar, and Grout ", Annual Book of ASTM Standards,2003
• ASTM C 618 – 03" Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete", Annual Book of ASTM Standards,2003.
• ASTM C 143/C 143M – 05a" Standard Specification for Slump of Hydraulic-Cement Concrete", Annual Book of ASTM Standards,2005
ASTM C 496/C 496M – 04" Standard Test Method for Splitting Tensile Strength of Cylindrical Concrete Specimens", Annual Book of ASTM Standards,2004
ASTM C 567-05A " Standard Test Method for Determining Density of Structural Lightweight Concrete", Annual Book of ASTM Standards,2005
• Badman, C., '' Interim Guidelines for the use of Self- Consolidating Concrete in PCI Member Plant '', PCI Journal, Vol.48, No.3, May/June 2003, pp.14-18
• BS1881, Part1, 1985, " Code of Practice for Design and Construction ", British Standards Institution
• BS 1881, Part 116, 1989, " Method for Determination of Compressive Strength of Concrete Cubes", British standards institution
• Druta, C., " Tensile Strength and Bonding Characteristics of Self-Compacting Concrete", M.SC. Thesis, Louisiana state university, August 2003, pp .125.
• EFNARC, "Specification and Guidelines for Self-Compacting Concrete", Feruary 2002, pp.32, www.efranice.org
• Justice, J.M., "Evaluation of Metakaolin for Use as Supplementary Cementitious Materials", M.Sc. Thesis, Georgia institute of Technology, April 2005, pp. 134
• M., Emborg, " Mixing and transport ", Final Report, Task 8.1, University of Paisly, June 2000, pp.65
• Mehta,P.K., and Monterio P.J, "Concrete: Microstructures, Properties and Materials", McGraw-Hill, United States of America, Third Edition, 2006, pp.684.
• Neville, A.M., "Properties of Concrete", Longman Group, Ltd., 4th and Final Edition, 2000, pp. 844
• Shindoh, T., and Matsuoka, Y., "Development of Combination- Type Self-Compacting Concrete and Evaluation Test Methods" Journal of Advanced Concrete Technology, V.1, No.1, April 2003, pp.26-36
• Okamura, H., and Ouchi, M., '' SelfCompacting Concrete'', Journal of Advanced Concrete Technology, Vol. 1, No.1, April 2003, pp.5-15.
Ouchi, M. "Self-Compacting Concrete: Development, Applications andInvestigations'', Nordic Concrete Research, 1999, pp.29-34
• The Self-Compacting Concrete European Project Group, "The European Guidelines for SelfCompacting Concrete", may 2005, pp.63