Corrosion-Resistance Characteristics of Concrete Containing Furfural
Main Article Content
Abstract
Corrosion inhibiting admixtures are unique among other methods to protect reinforced concrete from corrosion damage. In this study, the effect of furfural on the fresh and hardened properties of concrete mixes of 35 and 45 MPa compressive strengths as well as the corrosion inhibition of furfural was evaluated. Furfural was added at different dosages (1, 2 and 3% by weight of cement) with and without superplasticizer (HRWR). Different electrochemical measurements were performed (Half-cell potential, Tafel plot and linear polarization resistance). Electrochemical measurements confirmed that furfural dramatically reduces the rate of corrosion; the inhibition efficiencies were 62.7 and 63.8 % due to 3% furfural addition to 35 and 45MPa-concretes respectively. Results also showed that the combined presence of furfural and HRWR was found to provide an excellent corrosion protection to steel.
Article Details
Section
How to Cite
References
ACI Committee 222, "Corrosion of Metals in Concrete,” ACI 222R-96, Manual of Concrete Practice,1996,30 pp.
Babaei ,K., "Evaluation of half-cell corrosion detection test for concrete bridge decks", Washington state department of transportation in cooperation with the United States department of transportation federal highway administration, Final report November 1986, 86 pp.
Beaudoin J.J. and Ramachandran V.S.,”Effect of Water Dispersible Polymers on the Properties of Superplasticized Cement Paste, Mortar, and Concrete”, Reprinted from CANMET/ACI "Superplasticizers and other chemical admixtures in concrete , " Proceedings of Third International Conference 1989,Ottawa, Canada, ACI SP119-12,pp. 221-242.
Mancio, M., Carlos,C. J., Zhang.J., Harvey,J.T., Monteiro,P. J. M., and Ali,A,” Laboratory Evaluation of Corrosion Resistance of Steel Dowels in Concrete Pavement Prepared for the California Department of Transportation,” Pavement Research Center Institute of Transportation Studies University of California Berkeley and University of California Davis March, 2005 Revised May 2005,161 pp.
Neville, A.M., "Properties of Concrete," Pearson Education Limited, Fourth and final edition, 2005, 843 pp.
Rasheeduzzafar,Dakhil,F.H.,AL-Gahtani,A.S.,ALSaadoun,S.S.and Bader,M.A., "Influence of Cement Composition on the Corrosion of Reinforcement and Sulfate Resistance of Concrete," ACI Journal ,Mar-Apr.1990,pp.114-122.
Singh,V.K., Singh, R.K. and Khatri ,S.D, " Effect of furfuryl alcohol on the properties of hydrated cement mortar", J. Mater. Res., Vol. 18, No. 5, May 2003, 10 pp.
Civjan, S.A., Lafave, J.M., Lovett, D., Sund, D.J.andTrybulski,J.," Performance Evaluation and Economic Analysis of Combinations of Durability Enhancing Admixtures (Mineral and Chemical) in Structural Concrete for the Northeast U.S.A., " Prepared for the New England Transportation Consortium, project No.97-2,2003, 165 pp.
Al-Hubboubi,S.K.,"Corrosion of Steel Reinforcement in High Performance Concrete Containing Local Slag and Corrosion Inhibitor," M.Sc. thesis, University of Technology,Iraq, 2001,113 pp.
Amin,Z.H., "Corrosion of Steel Reinforcement in High Performance Concrete Containing RHA and Corrosion Inhibitor ", M.Sc thesis ,University of Technology,Iraq, ,2001, 126 pp.
Al – Ta’ie, S. A.," Durability of Concrete Incorporating Corrosion Inhibitor and AirEntraining Agent Exposed to Cl - + SO4-- Solution", M.Sc thesis ,University of Technology,Iraq, 2005, 108 pp.
Brown,M.C. , "Assessment of Commercial Corrosion Inhibiting Admixtures for Reinforced Concrete ",M.Sc. thesis ,Virginia Polytechnic Institute and State University, Civil and Environment Engineering , Blacksburg ,Virginia , Nov. 1999, 92 pp.
Trejo,D, Halmen,C and Reinschmidt,K., "Corrosion Performance Tests for Reinforcing Steel in Concrete:Technical Report,” Performed in cooperation with the Texas Department of Transportation and the Federal Highway Administration October 2008 Published: October 2009,209 pp