Impact of Glass Waste on the Flexural, Compressive, and Direct Tension Bonding Strengths of Masonry Bricks
محتوى المقالة الرئيسي
الملخص
The waste material problem in today's world has become a major topic affecting all sectors of human life. Researchers are interested in providing solutions for each kind of waste material. Waste glass is one of the waste materials whose amounts increase daily. This article deals with two types of modified cement mortar with glass granular in the masonry wall to find their effect on the wall's property (direct tensile, flexural, and compressive bond strength). Seven different mixes were prepared according to the used glass granular ratio (three mixes contained white glass with 15, 20, and 25% while three of them contained green glass granular 5, 10, and 15%, and the last mix was a controlled mix which contains no glass granular).Based on the obtained result, the used white glass granular provides optimum compression and direct tensile bond strength when 20% of sand is replaced with white glass granular; optimum direct tensile bond value was obtained, which increased by 1.4% and increased compressive strength by 13.08% compared to control mortar. Green glass granular provides optimum compression and direct tensile bond strength when 10% of sand is replaced, direct tensile strength by 1.02%, and increased compressive strength by 3.7% compared to control mortar. The increase of the used waste glass granular in the mortar decreases flexural bond strength, and the amount of decrease depends on the chemical glass compositions.
تفاصيل المقالة
كيفية الاقتباس
تواريخ المنشور
المراجع
Abdulhameed, H., Mansi, A., Mohammed, A., Abdulhameed, A., & Hanoon, A. (2021, December). Study the use of Nano-limestone and Egg-shell Ash in Eco-friendly SCC: an Experimental and Statistical Evaluation Based on Computer Programming. In 2021 14th International Conference on Developments in systems Engineering (DeSE) (pp. 509-514). IEEE.
Abdulhameed, A. A., Al-Zuhairi, A. H., Al Zaidee, S. R., Hanoon, A. N., Al Zand, A. W., Hason, M. M., & Abdulhameed, H. A. (2022). The Behavior of Hybrid Fiber-Reinforced Concrete Elements: A New Stress-Strain Model Using an Evolutionary Approach. Applied Sciences, 12(4), 2245.
Abaas, tahseen and K Abbas , D. Z. . (2022) “Production Load–bearing Concrete Masonry Units by Using Recycled Waste Crushed Clay Bricks; A Review”, Journal of Engineering, 28(10), pp. 13–27. doi: 10.31026/j.eng.2022.10.02.
Abdulhameed, A. A., Hanoon, A. N., Abdulhameed, H. A., Banyhussan, Q. S., & Mansi, A. S. (2021). Push-out test of steel–concrete–steel composite sections with various core materials: behavioural study. Archives of Civil and Mechanical Engineering, 21(1), 1-21.
Al shemaree, zainab and Aljalawi, N. . (2022) “Some properties of Reactive Powder Concrete Contain Recycled Glass Powder”, Journal of Engineering, 28(10), pp. 42–56. doi: 10.31026/j.eng.2022.10.04.
Altufaily, M. A. M., & Abdulhussein, T. B. (2019). Reuse of Crushed Glass and Aluminum Filings Wastes as Partial Replacement of Sand in Concrete Mixture. International Journal of ChemTech Research, 12(1), 329-338.
ASTM C29 / C29M-17a, Standard Test Method for Bulk Density (“Unit Weight”) and Voids in Aggregate, ASTM International, West Conshohocken, PA, 2017, www.astm.org
ASTM C33 / C33M-13, Standard Specification for Concrete Aggregates, ASTM International, West Conshohocken, PA, 2013, www.astm.org
ASTM C62-13a, Standard Specification for Building Brick (Solid Masonry Units Made From Clay or Shale), ASTM International, West Conshohocken, PA, 2013, www.astm.org
ASTM C67-17, Standard Test Methods for Sampling and Testing Brick and Stractural Clay Tile, ASTM International, West Conshohocken, PA, 2017, www.astm.org
ASTM C109 / C109M-21, Standard Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50 mm] Cube Specimens), ASTM International, West Conshohocken, PA, 2021, www.astm.org
ASTM C115 / C115M-10e1, Standard Test Method for Fineness of Portland Cement by the Turbidimeter (Withdrawn 2018), ASTM International, West Conshohocken, PA, 2010, www.astm.org
ASTM C117-17, Standard Test Method for Materials Finer than 75-μm (No. 200) Sieve in Mineral Aggregates by Washing, ASTM International, West Conshohocken, PA, 2017, www.astm.org
ASTM C128-15, Standard Test Method for Relative Density (Specific Gravity) and Absorption of Fine Aggregate, ASTM International, West Conshohocken, PA, 2015, www.astm.org
ASTM C136 / C136M-19, Standard Test Method for Sieve Analysis of Fine and Coarse Aggregates, ASTM International, West Conshohocken, PA, 2019, www.astm.org
ASTM C150-05, Standard Specification for Portland Cement, ASTM International, West Conshohocken, PA, 2005, www.astm.org
ASTM C187-16, Standard Test Method for Amount of Water Required for Normal Consistency of Hydraulic Cement Paste, ASTM International, West Conshohocken, PA, 2016, www.astm.org
ASTM C188-17, Standard Test Method for Density of Hydraulic Cement, ASTM International, West Conshohocken, PA, 2017, www.astm.org
ASTM C191-19, Standard Test Methods for Time of Setting of Hydraulic Cement by Vicat Needle, ASTM International, West Conshohocken, PA, 2019, www.astm.org
ASTM C305-20, Standard Practice for Mechanical Mixing of Hydraulic Cement Pastes and Mortars of Plastic Consistency, ASTM International, West Conshohocken, PA, 2020, www.astm.org
ASTM C321-12, Standard Test Method for Bond Strength of Chemical-Resistant Mortars, ASTM International, West Conshohocken, PA, 2012, www.astm.org
ASTM C778-17, Standard Specification for Standard Sand, ASTM International, West Conshohocken, PA, 2017, www.astm.org
ASTM C1314-16, Standard Test Method for Compressive Strength of Masonry Prisms, ASTM International, West Conshohocken, PA, 2016, www.astm.org
ASTM C1329 / C1329M-16a, Standard Specification for Mortar Cement, ASTM International, West Conshohocken, PA, 2016, www.astm.org
ASTM D1293-18, Standard Test Methods for pH of Water, ASTM International, West Conshohocken, PA, 2018, www.astm.org
ASTM E518-15, Standard Test Method for Flexural Bond Strength of Masonery, ASTM International, West Conshohocken, PA, 2015, www.astm.org
Churilov, S., & Dumova-Jovanoska, E. (2010). In-plane shear behaviour of unreinforced masonry walls. In Proceedings of the 14th European conference on earthquake engneering, 30th Aug–3rd Sept, Ohrid, FYROM.
Dehghan, S. M., Najafgholipour, M. A., Baneshi, V., & Rowshanzamir, M. (2018). Mechanical and bond properties of solid clay brick masonry with different sand grading. Construction and Building Materials, 174, 1-10.
Incerti, A., Rinaldini, V., & Mazzotti, C. (2016, June). The evaluation of masonry shear strength by means of different experimental techniques: A comparison between full-scale and laboratory tests. In Proceedings of the 16th international brick and block Masonry conference, Padova, Italy.
Kamal, O. A., Hamdy, G. A., & El-Salakawy, T. S. (2014). Nonlinear analysis of historic and contemporary vaulted masonry assemblages. HBRC Journal, 10(3), 235-246.
Lourenço, P. B. (1998). Experimental and numerical issues in the modelling of the mechanical behaviour of masonry.
Maheri, M. R., Motielahi, F., & Najafgholipour, M. A. (2011). The effects of pre and post construction moisture condition on the in-plane and out-of-plane strengths of brick walls. Materials and Structures, 44(2), 541-559.
Ogundairo, T. O., Adegoke, D. D., Akinwumi, I. I., & Olofinnade, O. M. (2019, November). Sustainable use of recycled waste glass as an alternative material for building construction–A review. In IOP Conference Series: Materials Science and Engineering (Vol. 640, No. 1, p. 012073). IOP Publishing.
Papadogeorgos, I., & K.. M. Schure. (2019). Decarbonisation options for the dutch container and tableware glass industry. PBL Netherlands Environmental Assessment Agency.
Sarangapani, G., Venkatarama Reddy, B. V., & Jagadish, K. S. (2005). Brick-mortar bond and masonry compressive strength. Journal of materials in civil engineering, 17(2), 229-237.
Sathiparan, N., & Rumeshkumar, U. (2018). Effect of moisture condition on mechanical behavior of low strength brick masonry. Journal of Building Engineering, 17, 23-31.
Sathiparan, N., Mayorca, P., & Meguro, K. (2008, October). Parametric study on diagonal shear and out of plane behavior of masonry wallettes retrofitted by PP-band mesh. In 14th world conference on earthquake engineering (pp. 13-17).
Soran Abdrahman Ahmad (2022). Evaluating the Effect of Waste Glass on the Mechanical Properties and Shear Bond Strength of Mortar. MSc thesis, College of Engineering-University of Sulimani.
Thamboo, J. A., & Dhanasekar, M. (2016). Nonlinear finite element modelling of high bond thin-layer mortared concrete masonry. International Journal of Masonry Research and Innovation, 1(1), 5-26.
Thamboo, J. A. (2020). Material characterisation of thin layer mortared clay masonry. Construction and Building Materials, 230, 116932.
The United States Environmental Protection Agency.(2018).US EPA ARCHIVE DOCUMENT Retrieved http: // www. epa. gov
Zeng, J. J., Zhang, X. W., Chen, G. M., Wang, X. M., & Jiang, T. (2020). FRP-confined recycled glass aggregate concrete: Concept and axial compressive behavior. Journal of Building Engineering, 30, 101288.