A STUDY EFFECT OF SOME VARIABLES IN TIG SPOT WELDING FOR (ALUMINUM – MAGNESIUM) ALLOY
محتوى المقالة الرئيسي
الملخص
The present work investigates the effect of some of the variables in spot tungsten inert gas shielded
welding (TIG Spot) for (Aluminum-Magnesium) alloy type(5052-O) which is non–heat treatable
alloy for its wide industrial uses and applications in field of welding technology.
TIG Spot welding was performed by using tungsten electrode (EWTh2)of diameter (3.2mm) and
DC current with direct polarity (DCSP) at constant shielded gas flow rate (15litre/min).
The welded specimens were tested by using the Instron machine to determine the maximum shear
force (shear strength ) of spot welded and to define the optimum conditions of spot welding
variables in relation to the weld current, weld time and arc length of welding to produce an
acceptable weld. The metallurgical changes of the weld zone and heat affected zone were studied
under optimum conditions of welding.
It has been shown that the increase in the welding current and welding time tends to increase the
maximum shear force and it reaches maximum value and then decreases with high currents and
long times. The maximum shear force was 2.4KN at welding current of (90) Amp , welding time
( 7)sec and arc length (1.6mm ) for 1mm thickness.
It was also found that the highest value of hardness ( 53.5 Hv) was at the center of the spot welded
and decreases gradually from the center of the weld spot towards the base metal.
تفاصيل المقالة
القسم
كيفية الاقتباس
المراجع
Abbass F. (2001), Study of TIG Spot in (Al-Mn) Alloy, MSC. Thesis , University of Technology ,.
Aidun D.K. (1985), Effect of Resistance Welding Variables On The Strength Of Spot Welded 6061-T4 Alloy, Welding Journal , Vol.64, No.12 , , PP.15-25.
Bolton W. (1998), Engineering Materials Technology, Butter Worth ,3rd ed. ,.
Brumpauph J.E. 1973" Welders Guide and Handbook " , Howard Wsas Co..
Filler Alloy Selection For aluminum welding, Google’s cache of http://www.alcotec.com/atfas.htm.
George Rowe- Alcotec Wire Corporation (2003), Essential Variables For MIG Welding Aluminum ,Svetsaren ,The ESAB Welding and Cutting Journal ,Vol.58, No.2 , PP.12-13.
Gupta R.P. (1995), Welder,Tech. India Publications,.
Haddad G.N. (1985), Temperature Measurement in Gas Tungsten Arc Welding, Welding Journal ,Vol.64, No.12 , ,PP.339S-342S.
Houldcroft P.T. (1977), Welding Process Technology, Cambridge University Press,.
Khanna O.P. (1980), Welding Technology, Dhawpatria Sans,.
Konolovanov U.A. (1986), Helium Arc Spot Welding of Aluminum , Sheet Structure, Welding Production , No.4 , , PP.14-15.
Little R.L. (1973), Welding and Welding Technology " McGraw Hill ING ,.
Lancaster J.F. (1986), The Physical Of Welding, 2nd edition , Bergamon Press, London,.
Lu M .and Kou S. (1988) , Power and Current Distribution in Gas Tungsten Arcs , Welding Journal, Vol.67 , No.2 , PP.29S-34S.
Metals Handbook (1985), Aluminum , Cleaning and Finishing , Vol.5 9th ,.
Stuart W.G. (1997), Advanced Welding, Macmillan Press LDT ,1st Published, Printed in Hong Kong,.