THE EFFECT OF COARSE AGGREGATE RATIO ON THE PROPERTIES OF NO FINE LIGHT WEIGHT CONCRETE
محتوى المقالة الرئيسي
الملخص
The main object of this work is to study the effect of coarse aggregate/cement ratio (A/C) on the property of no fine concrete. In this work, three ratio of A/C were used (6, 9 and 12 by weight).The cement content is maintained constant (125kg/m3) while the w/c ratio ranges from (0.39 to 0.55 by weight). Tests are carried out on hardened concrete to investigate the effect of coarse aggregate/cement ratio on the compressive strength, absorption%, density, porosity%, ultrasonic pulse velocity, acoustic impedance of mixes.
The results showed that increasing the percentage of A/C ratio by weight from 6 to 12 for the used mixes reduces the compressive strength, ultrasonic pulse velocity and acoustic impedance, on the other hand the porosity and the absorption percentage, increase with increasing ratio of A/C for all studied mixes.
At 28 days the compressive strength , ultrasonic pulse velocity and acoustic impedance tests with A/C ratio of (12) are (2.8.MPa), (2km/sec) and (3×106 Kg/(sec.m2)) respectively while decreasing the ratio to (6) improves these properties to (9.3MPa), (3km/sec) and ( 5.7 ×106 Kg/(sec.m2)) respectively On the other hand the porosity and the absorption % decrease with decreasing the ratio of A/C for all studied mixes . At 28 days the porosity and the absorption % with A/C ratio of (12) are (40%) and (2.7%) respectively with decreasing the ratio to 6 decrease these properties to (19%) and (1%) respectively.
The densities of the mixes were tested. At 28 days the density with A/C ratio of (12) are (1512 kg/m3 )with decreasing the ratio to 6 increase the density to(1907 kg/m3 )
Based on the analysis of experimental results, several graphs and tables have been prepared to study the properties of no fine concrete
تفاصيل المقالة
كيفية الاقتباس
تواريخ المنشور
المراجع
Harber, P., J., " Applicability of No-Fines Concrete as a Road Pavement " University of Southern Queensland Faculty of Engineering and Surveying , October 2005.
Neville, A.M., “Properties of Concrete”, Longman Group, Ltd., Fourth Edition, 2002, PP.412-423.
ACI 213R – 87 , Guide for structural lightweight aggregate concrete , ACI Manual of concrete practice, part 1: Materals and General properties of concrete 1994, 27 pp.
Meininger , R,. C,. " No-Fines Pervious Concrete for Paving " Concrete International : Design and Construction. Vol. 10. No. 8 August pp 20-27 .
Abadjieva , T and Sephiri , P., " Investigation on Some Properties of No- Fines Concrete " Department of Civil Engineering University of Botswana.
Al-Rubayi, I. ,T.,K., “Using of local materials to produce light weight paving units for Baghdad municipality projects ”, M.Sc. Thesis, University of Technology, May 2007, pp.169-171.
IOS NO. 5 : 1984 , Iraqi cement standard for Portland cement.
IOS NO. 45: 1984 , Iraqi standard for aggregate.
B.S.1881, Part 116, 1989, “Method for Determination of Compressive Strength of Concrete Cubes”, British Standards Institution, P.3.
B.S.1881, Part 113, 1983, “Method for making and curing no- fines test cubes ”, British Standards.
ASTM C642-97,“Standard Test method for Density, Absorption, and Voids in Hardened Concrete” , ASTM Standards, .04.02,2003,PP.1-3.
Al-Zangy, R. , A., “Properties Of Low Density Concrete ”, M.Sc. Thesis, University of Technology, May 2003, p.115.
Naik , T. R., Malhorta , V. M. , and Popvics , J. S. , “The Ultrasonic Pulse Velocity Method ”,CRC Press LLC 2004 P. 7.
ASTM C597-02 “Standard Test Method for Pulse Velocity Through Concrete”, Annual Book of ASTM Standard, Vol. 04-02, 2002.
Lin , Y. , Kuo , S. F. , Hsiaio , C. , and Chao , P. L. ,“Investigation of Pulse Velocity – Strength Relationship of Hardened Concrete” , ACI Materials Journal , V. 104, No. 4, July – August 2007, PP.344-350.
AL- Jeelawi , N., M., F., " properties of light weight concrete with a view to thermal insulation and acoustic impedance " M.Sc. Thesis, University of Baghdad, August 1997, pp.78 - 79.