MECHANICAL DEGRADATION OF HIGH MOLECULAR WEIGHT POLYMER WITH SURFACTANT ADDITION IN A ROTATING DISK APPARATUS
محتوى المقالة الرئيسي
الملخص
Mechanical degradation hampers the practical usage of polymers for turbulent drag reduction
application. Mechanical degradation refers to the chemical process in which the activation energy of
polymer chain scission is exceeded by mechanical action on the polymer chain, and bond rupture
occurs. When a water-soluble polymer and surfactant are mixed in water solution, the specific structures
(aggregates) are formed, in which polymer film is formed around micelle. In this work, Xanthan gum (XG) –
Sodium lauryl ether sulfate (SELS) complex formation and its effect on percentage viscosity reduction
(%VR) was studied. It was found that SELS surfactant reduced the mechanical degradation of XG much
more efficiently than this polymer alone. Xanthan Gum (XG) has been tested for its shear stability and
degradability. 0.5% and 1.0 % by weight concentration solutions were exposed to shear stirring at different
speeds and time; also 0.5% through 1.5% by weight concentration solutions of SELS were added to XG
solutions to determine the ability of SELS to reduce the mechanical degradation of XG. It has been noticed
by measuring the percentage viscosity reduction (%VR) of the mixture of XG-SELS that the % VR
decreases when added this surfactant to XG polymer
تفاصيل المقالة
كيفية الاقتباس
تواريخ المنشور
المراجع
- C.A. Kim, D.S. Jo, H.J. Choi, C.B. Kim and M.S. Jhon, " A high-precision rotating disk apparatus for drag reduction characterization", Polymer Testing 20 (2001) 43–48.
- J.-I. Sohn, C.A. Kim, H.J. Choi and M.S. Jhon, " Drag-reduction effectiveness of Xanthan Gum in a rotating disk apparatus", Carbohydrate Polymers 45 (2001) 61-68.
- H.J. Choi, C.A. Kim and M.S. Jhon, " Universal drag reduction characteristics of polyisobutylene in a rotating disk apparatus", Polymer 40 (1999) 4527–4530.
- H. J. Choi, C. A. Kim, J. H. Sung, C. B. Kim, W. Chun and M. S. Jhon, " Universal drag reduction characteristics of saline watersoluble poly(ethylene oxide) in a rotating disk apparatus ", Colloid Polym Sci 278 (2000).
- Ketan Prajapati, “Interactions between drag reducing polymers and surfactants”, M.Sc thesis, Waterloo, Ontario, Canada, 2009.
- Marwa F. Abdul Jabbar, “The Influence of Mechanical Effects on Degradation of Drag Reducing Agents”, M.Sc thesis, Nahrain University, Baghdad, Iraq, 2008.
- Matthew W. Liberatore, Seunghyun Baik, Anthony J. McHugh and Thomas J. Hanratty, " Turbulent drag reduction of polyacrylamide solutions: effect of degradation on molecular weight distribution", J. Non-Newtonian Fluid Mech. 123 (2004) 175–183.
- Nam-Jin Kim, Jae-Yong Lee, Seok-Mann Yoon, Chong-Bo Kim and Byung-Ki Hur,“Drag Reduction Rates and Degradation Effects in Synthetic Polymer Solution with Surfactant Additives”, Journal of industrial and engineering chemistry Vol. 6, No. 6, November 2000, 412-418.
- V.N. Kalashnikov, “Degradation accompanying turbulent drag reduction by polymer additives”, J. Non-Newtonian Fluid
Mech. 103 (2002) 105–121.